Luster

Lightless

Theoretical spreading rate

330g/m2, 5.55m2/L (calculated in 60μm dry film, excluding the loss)

Specific gravity:

About 1.83

Drying time

23±2℃: surface dryness≦10 min, solid dryness≦24h

Entirely cured

23±2℃:3d

Flash point

13℃

Storage period

12 months for Component A; 6 months for Component B

Construction Instruction

Mixing ratio

Component A ( paint ): Component B ( curing agent )=30:7.5

Maturing time

23±2℃; 0.5~1h

Service life

23±2℃; 8h

Construction method

High-pressure siphon spray; normal spray;  manual painting;  roller coating  

Diluent

X-11inorganic zinc rich coatingdiluent

Maximal dilution amount

Spray orifice

Spray pressure

Tool washing

X-11inorganic zinc rich coatingdiluent

Film coating thickness

Wet film: 180μm                     Dry film: 120μm

Coating interval

Surface treatment

＊The steel surface is required to be subjected to shotblasting or sandblasting method for treatment; as anti-rust paint, the coating surface is required to reach Grade Sa2.5 of Sweden Derusting Standard.

＊As anti-rust paint, the coating surface is required to reach Grade Sa3 of Sweden Derusting Standard.

＊The roughness reaches40-70μm.

Construction condition

The temperature of substrate must be 3℃ higher than dewing point, and the relative humidity must be less than 50%.

Finishing paint

Epoxy resin coating, epoxy asphalt coating,  oxide rubber coating,alkyd resin coating, polyurethane coating, highly chlorine polyethylene coating; the finish paint may not also be coated.

Packing Specification

30Kg/20L per barrel for Component A; 7.5Kg/10L per barrel for Component B

Considerations

＊Since the content of zinc power is high, while allocating, it is suggested to employ the mechanical stirring to uniformly stir Component A, after that, add Component B and stir uniformly.

＊When the substrate temperature is≧30℃ but doesn’t exceed 60℃, in order to avoid dry spraying, the diluent must be added and regulated until no dry spraying;

＊Prior to coating the next pass of paint, the zinc salt on the surface must be eliminated thoroughly, otherwise, the adhesion force between paint film layers shall be affected.

Safety guide  

Avoid breathing solvent steam or paint fog for a long term; the skin and eye can’t contact this product; while constructing in the narrow place or poorly ventilated place, the forced ventilation must be provided; while constructing, the protective articles should be worn.

Annotation

＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure siphon spray;

＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

＊If above data is changed, the data is based on the latest instruction, without prior notification.